Jump to content

Marcia Selsor

  • Content count

  • Joined

  • Last visited

  • Days Won


Marcia Selsor last won the day on August 31

Marcia Selsor had the most liked content!

Community Reputation

1,301 Excellent

1 Follower

About Marcia Selsor

Contact Methods

  • Website URL
    http://www.marciaselsorstudio.com , http://www.lameridiana.fi.it/pottery-workshops-marcia-selsor-36-17.htm

Profile Information

  • Gender
  • Location
    Red Lodge, Montana
  • Interests
    "I have been working in clay since 1966. -an industrial design major in a ceramics elective. I got hooked!. I love the fire, kilns, tactile surfaces and the comraderie of the folks who live with this humbling medium. My interests in Clay include dynamics of Kiln designs, Glaze Chemistry, Throwing, building kilns, and developing tools for new forms and textures, alternative firing processes and the World History of Ceramics. On a non-ceramics note I enjoy cooking and gardening, travel, museums observations of nature including wild horses and birds incorporating them into my art. Moved back to Montana where I'll be able to visit the wild horse herds in the Pryor Mountains.


Recent Profile Visitors

998,554 profile views
  1. new forum, what i dislike

    Sorry Mea, but I just got back from Italy and missed all the discussion. Holly Goring told me to contact Steven because she is unaware that any changes were made. Thanks for the details. I don't even want to deal with the new forum. Marcia
  2. new forum, what i dislike

    true. but he should be aware of the problems so many people are having. I just asked him to review the thread of what people are having problems with. PLEASE CONTACT OUR MODERATORS IF YOU ARE HAVING PROBLEMS. THEY ARE TRYING TO ASSIST EVERYONE. Thanks Mea ,
  3. new forum, what i dislike

    I was off for 2 weeks. Came back to this new format and don't have a clue. Thanks for all the help from others. Steve Hecker is the new administrator in charge of this. Send your requests directly to him. Marcia
  4. Raku Question

    Raku clay does not mature at low temperature. That it why it works in raku. Typically it can go to ^6 or even ^9 but you need to test. It is not really a lowlier type of clay, it is a porous open body at raku temperature to deal with the thermal shock. That is why groggy stoneware works. Marcia
  5. Raku Question

    I think it may depend on the specific clay body. The only white ^6 stoneware I ever used was a "vessel 6" which we mixed ourselves when I taught in Billings. I don't think we fired it in raku but we did fire out ^6 stoneware that we mixed.
  6. Raku Question

    I agree with John about anything fired to maturity will not withstand the thermal shock of a raku firing. If it were fired to bisque , np problem. But fired to ^6 is a big one. Marcia
  7. Raku Question

    Lee, If you have some ^6 clay fired to bisque between ^09 to ^04 you should not have any problems firing to a raku temperature of ^05 or ^06. Marcia
  8. how do I create an album in my gallery?

    Lee, Is this in your personal gallery? I often respond to specific questions with a link to an image in my gallery. I don't want a link to a reply on the forum because it will get lost.hat was nice about members galleries. Marcia
  9. how do I create an album in my gallery?

    Thanks Pres. Maybe its the jet lag nut this new format seems extremely complex to navigate. tried it. Had the images there, then a page came up and said drag the images here. ? Marcia
  10. Alternative Firing Workshop at La meridiana 2017

    here are some results from my Alternative Firing workshop at La Meridiana. I covered making quick terra sig, crackled surfaces using sodium silicate, preparing foil sagger with metallic salts, preparing ceramic sagger with sawdust, wire, banana skins, etc.
  11. Obvara results with martina's piece in front

    From the album Alternative Firing Workshop at La meridiana 2017

    One student's successful try at sodium silicate crackle