  1. The Genesis controller has many great features. My experience with it did not end up good and I returned it and they gave me a full refund. As Dick White said they give no information as to what some of there software changes mean to how it will react. I felt like I was doing there testing in the field for them and that this should have been done before it left the factory. I finally gave up when they tried to convince me that the cycling was due to stray coming in on the thermocouple even though I kept telling them the old V6 worked perfectly. I now have an industrial controller that
  2. It looks like the latest software 3.18.9 fixes the problems with the controller. David
  3. I bought a Genesis controller as an upgrade to my Bartlett V6-CF. The first firing with it just did what ever it wanted and overfired everything. I called Bartlett Co. and their Technician was only interested in proving their was nothing wrong with the controller, it was my programing. Finally after firing twice more with just shelves and posts and cones in the kiln I pulled the controller and put the original V6-CF back in and fired a load of pots successfully. Today I called Bartlett to return the controller, and was put thru to Dave Bartlett, he said a lot of upgrades had been made on
  4. www.LagunaClay.com have parts including a motor kit for the Model K. It is a great wheel and lasts for years.
  5. You could use a 6 cup and tile blend of A base glaze and B base glaze plus 5% stain. 150 grams base for A and 150 grams base plus 5% stain for B Use a syringe , 1 50cc A, 2 40cc A 10cc B,3 30cc A 20ccB, 4 20cc A 30cc B, 5 10cc A 40cc B. 6 50cc B

    1. Joseph Fireborn

      Joseph Fireborn

      Thanks, I will think about this. I am not sure I directly understand it I need to write it down on paper.

  6. I use containers 1 quart from home depot for the 4 corners. The individual cups are used yogurt cups about 6 oz. The test tile, because I am interested in vertical tests are extruded test tiles long enough to make 5 tests per tile times 7 tiles for the 35 grid. I only use 300 gram batch for the corners. The syringe is 60 cc McKesson Syringe without needle order 102-SC60C20. Each cup has 48 Milli Litres per sample. David
  7. David Woodin

    David Woodin

    Satin glaze cone t electric and wood fired
  8. From the album: David Woodin

    same satin glaze wood fired cone 10
  9. The Currie method is great for revealing what other glazes you might have in the grid from a known glaze. So he takes a known glaze and makes extreme changes in the Alumina/ silica. But if you want to make a glaze from scratch take a look at Robin Hoppers book "The Ceramic Spectrum" The information I posted was a method to look at two colorants and actually uses the same % as the Currie grid after you make the 4 corners using a known glaze. You don't do anything with the alumina or silica. David
  10. I usually make a 20 grid but 35 grid would work fine. A = base glaze + 8% Iron Oxide: B same base glaze + 8% Iron Ox.& 10% rutile; C same base glaze no colorant: D 10% Rutile. This gives a line blend from A to C for iron; A to B iron stays at same value but it cross blends with Rutile :C to D line blend for Rutile: This line blend cross blends with iron B to D. This is impossible to explain but the top row 1 thru 4 Iron is 8%, but 2 to 4 rutile is #2 = 3.33%R + 8% Fe,# 3= 6.67% Rutile + 8% Fe, # 4= 10% Rutile + 8% Fe. Anyway it is a good method for testing 2 colorants and depending on
  11. Have you ever tried taking a glaze that you use and run the Currie method on it? You may be surprised that there are many more good glazes in the grid. Also there are some other very good ways to test colorants. David
  12. I would be inclined to change out the controller for a Barlett. The kiln itself will be fine but electronics have changed a lot in 22 years and you may be fighting problems due to drying out of compenents, parts no longer made etc. Euclids can help with getting you up to speed with a new Barlett and possibilily zone control. David
  13. No the fluxes don't have to add up to 100. You are to take a glaze and leave out the clay and Silica, if it has any, and just put in the flux material even though they may have some AL203 and SiO2 in them. Ex: Custer feldspar. The calculation on the web site is going to add clay and silica to the batch. I usually make test tiles because I want to see what happens on vertical surfaces. David
  14. You probably would do better by trying to hold the top temperature instead of cycling up and down. You can reglaze the pieces and fire again with a hold. I didn't think that clay was used in the ancient recipes. David
  15. I use Matrix limits, Insight limits, and Food safe Cone 6, Cone 10 limits. Insight and Matrix allow for cones other than Cone 6 and Cone 10. I usually fire to cone 7 in the electric kiln and in the gas kiln cone 9. That way I only need one stoneware clay body. David
  16. Matrix does have the Currie grid and also you can make your own grid. I make my own grid and make the corners match the Al/Si limits for whichever cone I am firing at. Matrix also has a very good method for testing colors used in glazes. David
  17. I have used the Currie 35 tile method quite often, but found that some of the tests were way outside the functional limits. I started making other tests inside the grid for AL/Si limits, which resulted in more good glazes. I use the Matrix glaze program to do this. David
  18. The timer and relay is supposed to pulse the middle section every 60 seconds. The elements themselves are never connected directly to the power from the kiln setter. The elements are controlled by the infinite switches or timer/relays which receive power from the kiln sitter. You will have to check each infinite switch and the timer/relays. If any elements are directly wired to the kiln sitter then their is a mistake in the wiring. Hopefully you can contact someone at Paragon. David
  19. Did someone try to install a controller for this kiln? The Paragon web site doesn't show anything but infinite switches. Did you buy the kiln from Paragon? More information is needed for this kiln and if it was modified then Paragon isn't responsible for it. You mentioned 2 cycle control?? David
  20. Ramp is either time to get from one temperature to another or set as degrees per hour. You mentioned holding for 30 minutes at top temperature, this would mean you probably fired hotter than Cone 04. Most bisque is at cone 06. If you fire sculpture or heavy pieces slow bisque is okay otherwise I would use fast bisque and save 3 hours total time. The Orton 3000 is a great controller and you should look into making your own programs David.
×
×