  1. I'm attracted to the whiteness and translucency and supposed strength of porcelain. Will I get this at cone 6 if I use a porcelain clay designed for it? I've been using cone 6 cream colored stoneware. Any ideas on what differences I'll notice working with it, firing it, and finishing it? I've heard porcelain is less forgiving... How do I clean the stoneware clay off my canvas table? So far, I've only used it for off white clays... Nothing like terra cotta, so I wouldn't think if be THAT much of an issue... Your thoughts?
  2. Hello y'all: I'm interested in non-food safe glazes, and wondered if you had ideas on things I could make that didn't involve food or drink. So far, I thought of: Vases Decorative bowls Windchimes? Plant pots Any other ideas? TA
  3. Hello-- I'm thinking of doing a figure with a crown, and I'd like the crown to be gold-ish, though being metallic is more important to me than being yellowy gold. In the end, I want the gold to look very worn, dirty, and antiqued. I don't want to paint it. Is there a glaze that would do the trick? Some wash? Goldleaf after firing? Thanks, TA
  4. I'm searching for a way to get a finish like that in the pictures attached. Both Oxide washes and Mason stains have been recommended. I did a little research, and it seems that a big benefit of Mason stains is that they are more "what you see is what you get." Given what I'm going for, does anyone have recommendations or information on the similarities/differences that might guide my decision? I could always use both, but I'm not sure when to use what. Thanks! TA
  5. How To Create A Finish Like This?

    The mason stains look interesting. How well do the colors stay at ^6?
  6. Opinions On What Glazes To Start With?

    For now I've decided to make my own glazes. They turned out pretty good! I'm also interested in the dry look of oxide washes...
  7. Nylon In Clay?

    Anyone work with this? I'm getting into sculpture and it seems pretty cool. I just finished making a batch. The biggest benefit I see touted is the ability to connect bone dry pieces. Are there other benefits? Anything I should know before I start? I can still single fire with it I assume. (I know about the smoke it creates.) Any tips or info would be helpful. Thanks!
  8. Oxide Stain: Cadmium At Cone 6?

    Bummer. Just posted a new thread for red suggestions.
  9. I just posted a thread about using cadmium, and was told that it was fugitive at ^6. Any other recommendations? This stain will be used for small details on sculpture, so I'm not concerned about toxicity. Ideally, the color would be valentine red. Thanks! TA
  10. Oxide Stain: Cadmium At Cone 6?

    Almost. Cadmium sulfoselenide
  11. Oxide Stain: Cadmium At Cone 6?

    I worked for quite awhile as a chemist and am aware of what I'm up against.
  12. I have some red cadmium, and I would like to get a nice red oxide stain. If I just mix a little cadmium with some frit, will this get me there at cone six? I heard there were some concerns with cadmium bleaching out higher temperatures. What are you guys think?
  13. I'm trying out some sculpture, and many of the resources use clay supports to hold up arms and things to help support their weight. They state that these will remain intact through the bisque firing. My question is, how do you keep the arm from sticking to the support? Obviously you wouldn't score and slip and not even press down on the piece, but it seems like they would stick together a little bit. If this happens is there a way to separate them without breaking the piece?
  14. Anyone know how to create a finish like that shown in the attached picture? I'm interested in trying out sculpture, and am attracted finishes like this. Specifically, I'm looking for something: Very thin, so the fine detail in the piece remains. Muted colors (but still color present) Matte Finish Fired--not painted. I like the permanency and durability of a fired "glaze" or finish. I've made a few of my own glazes now, and they've turned out well... but they look like a typical glaze. Any ideas?
  15. Help! Not All Elements Are Working In My Kiln.

    I found two breaks in the elements and repaired them quite simply. Everything seems to be working now
×