Adding Self-Harening Clay To Bisque Fired Pieces

Recommended Posts

If you can tell us why you want to do this we might be able to give you some

other ideas for it.

 

 

I made slip cast pots. After firing I realized there are sections I want to add texture to.

Could have added w/slip or glazes prior to firing but didn't.

I know there are cold glazes that can create rock/crackle textures but not quite what I want.

I'm looking to see if I can sculpt onto the pots with a like material.

Share this post


Link to post
Share on other sites

For textures on already fired pieces you can also use a vitreous slip.It can be added to biscuit ware or It can even be used on a (thin)glazed surface.You have to fire the work again.

 

 

Very interesting - thanks.

Share this post


Link to post
Share on other sites

For textures on already fired pieces you can also use a vitreous slip.It can be added to biscuit ware or It can even be used on a (thin)glazed surface.You have to fire the work again.

 

 

Very interesting - thanks.

 

 

Is there a specific vitreous slip product/brand or can I apply the slip used for casting?

Share this post


Link to post
Share on other sites

Like Chris, my personal philosophy is to chalk it up to experience and move on, of course that's just me. Everyone makes culls at one time or another and it should not be considered a mistake, it just was an unanticipated event. My excursions from desireability usually become grog. Perhaps you can do something else with the ones you've bisqued and add an interesting glaze design and they just become something else.

 

Best regards,

Charles

Share this post


Link to post
Share on other sites

Thanks to all those who have responded to my questions!

I have made quite a lot of my pots/vessels knowing I will sacrifice a few to experimentation.

It will be a good to test a pot or 2

=)

Share this post


Link to post
Share on other sites

Instead of using a vitrious slip(which will crack when applied to thick),you can also attach greenware particles to glazed or fired ware.Because they keep 'floating' on top of the glaze during firing they don't crack.Glaze will fix the particles to the piece .

Share this post


Link to post
Share on other sites

I have used paper clay on the inside and bottom of a bisque fired pot that had an S crack. It worked and you cannot even tell the crack was there!

 

 

The paper clay will adhere to bisque fired slip? Nice!

 

Thanks.

Share this post


Link to post
Share on other sites

Instead of using a vitrious slip(which will crack when applied to thick),you can also attach greenware particles to glazed or fired ware.Because they keep 'floating' on top of the glaze during firing they don't crack.Glaze will fix the particles to the piece .

 

 

Thanks!

Share this post


Link to post
Share on other sites

I have used paper clay on the inside and bottom of a bisque fired pot that had an S crack. It worked and you cannot even tell the crack was there!

 

 

 

Did you put it through another bisque fire before glazing? I have a large bowl that I handbuilt that cracked slightly on the edge inward about 2 inches. Not a wide crack. I was thinking about putting some paper clay and keeping it for myself. I didn't know if I needed to fire it again before the glaze firing.

 

 

Share this post


Link to post
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

Sign in to follow this  

×
×
  • Create New...

Important Information

By using this site, you agree to our Terms of Use.