Primus-P Feldspar

Recommended Posts

I used to use a potash feldspar from Mexico called Primus. Now it is no longer available and I've switched back to Custer, but it changed my main glaze and I'm having big problems with it (blistering). Does anyone know if it might still be available somewhere in the US? Or, which feldspar it would be best for me to use now?

Share this post


Link to post
Share on other sites

Sadly, Custer is not what it used to be. A few years ago, people began noticing the very problems you are having - blistering, pin holes, lack of melt -  with glazes containing significant amounts of Custer.  It was finally traced to an unannounced and as yet unacknowledged (by Pacer Corp, the producer of Custer) change in the properties of Custer. Compared to 5 or 10 years ago, the current product has about a quarter less potassium (which belies it being called a potash spar...), an eighth less alumina, and about 6% more silica than before. That makes for an unfluxed, non-melting, pin holing glaze. To restore your glaze, you need to reformulate the recipe using more (much more) Custer and adjusting the silica downward. This is easy enough to figure out if you are facile with glaze calculation software but tricky to stumble around with line blends and other traditional glaze testing methods. If you have glaze calculation software, I can give you the new material analysis, or if you aren't comfortable with glaze calculations, post your glaze recipe and I'll recalculate it for you.

Share this post


Link to post
Share on other sites

Thanks,

I don't have the glaze calculation software, but would rather not publish this recipe online. But thanks for the tips. If you google Margaret Kunzler you can get my information on Siskiyou Arts Council webpage. Another question I have about possible changes in this glaze is the barium. Is there a big difference between Chinese barium and German Barium? Another possible problem is that I added a little chlorine bleach to the bucket because of growth of green slime. (Could this affect the glaze?) I'm going to run a bunch of tests. I will also try G-200 feldspar. Strangely enough, this matte glaze has become more melted with Custer. I'm thinking of removing some of the flux.

 

Thanks again,  Margaret

Share this post


Link to post
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now
Sign in to follow this  

×